Conductive Noncontact (NSC), Contact (CSC) and 4-Lever (XSC) silicon probes
Brand:
Category:
Pyramidal silicon etched probes* with conductive platinum or gold coatings are suitable for a wide range of electrical applications of AFM. Gold and platinum coatings are inert, which makes these probes applicable for many experiments in biology and chemistry.
Pt coated resulting tip radius ................................... < 30 nm
Pt overall coating ............................................ 30 nm
Cr-Au coated resulting tip radius .................................... < 35 nm
Au overall coating ................................................. 30 nm
Cr overall sublayer ............................................... 20 nm
Technical Features
Serie Cantilever | Rivestimenti | Lunghezza ±5µm | Larghezza ±3µm | Spessore ±5µm | Freq. Rison. kHz Tipica | Freq. Rison. kHz Range | Const. Force Nm Tipica | Const. Force Nm Range |
---|---|---|---|---|---|---|---|---|
HQ:NSC14 | /Cr-Au /Pt | 125 | 25 | 2.1 | 160 | 110 - 220 | 5.0 | 1.8 - 13 |
HQ:NSC15 | /Cr-Au /Pt | 125 | 30 | 4.0 | 325 | 265 - 410 | 40 | 20 - 80 |
HQ:NSC16 | /Cr-Au | 225 | 37.5 | 7.0 | 190 | 170 - 210 | 45 | 30 - 70 |
HQ:CSC17 | /Cr-Au /Pt | 450 | 50 | 2.0 | 13 | 3-17 | 0.18 | 0.06 - 0.40 |
HQ:NSC18 | /Cr-Au /Pt | 225 | 27.5 | 3.0 | 75 | 60 - 90 | 2.8 | 1.2 - 5.5 |
HQ:NSC19 | /Cr-Au /Pt | 125 | 22.5 | 1.0 | 65 | 25 - 120 | 0.5 | 0.05 - 2.3 |
HQ:NSC35 | 3 leve | |||||||
HQ:NSC35 leva A | /Cr-Au /Pt | 110 | 35 | 2.0 | 205 | 130 - 290 | 8.9 | 2.7 - 24 |
HQ:NSC35 leva B | /Cr-Au /Pt | 90 | 35 | 2.0 | 300 | 185 - 430 | 16 | 4.8 - 44 |
HQ:NSC35 leva C | /Cr-Au /Pt | 130 | 35 | 2.0 | 150 | 95 - 205 | 5.4 | 1.7 - 14 |
HQ:NSC36 | 3 leve | |||||||
HQ:NSC36 leva A | /Cr-Au /Pt | 110 | 32.5 | 1.0 | 205 | 130 - 290 | 8.9 | 2.7 - 24 |
HQ:NSC36 leva B | /Cr-Au /Pt | 90 | 32.5 | 1.0 | 130 | 45 - 240 | 2 | 0.2 - 9 |
HQ:NSC36 leva C | /Cr-Au /Pt | 130 | 32.5 | 1.0 | 65 | 25 - 115 | 0.6 | 0.06 - 2.7 |
HQ:CSC37 | 3 leve | |||||||
HQ:CSC37 leva A | /Cr-Au /Pt | 250 | 35 | 2.0 | 40 | 30 - 55 | 0.8 | 0.3 - 2 |
HQ:CSC37 leva B | /Cr-Au /Pt | 350 | 35 | 2.0 | 20 | 15 - 30 | 0.3 | 0.1 - 0.6 |
HQ:CSC37 leva C | /Cr-Au /Pt | 300 | 35 | 2.0 | 30 | 20 - 40 | 0.4 | 0.1 - 1 |
HQ:CSC38 | 3 leve | |||||||
HQ:CSC38 leva A | /Cr-Au /Pt | 250 | 32.5 | 1.0 | 20 | 8 - 32 | 0.09 | 0.01 - 0.36 |
HQ:CSC38 leva B | /Cr-Au /Pt | 350 | 32.5 | 1.0 | 10 | 5 - 17 | 0.03 | 0.003 - 0.13 |
HQ:CSC38 leva C | /Cr-Au /Pt | 300 | 32.5 | 1.0 | 14 | 6 - 23 | 0.05 | 0.005 - 0.21 |
HQ:XSC11 | 4 leve | |||||||
HQ:XSC11 leva A | /Pt | 500 | 30 | 2.7 | 15 | 12 - 18 | 0.2 | 0.1 - 0.4 |
HQ:XSC11 leva B | /Pt | 210 | 30 | 2.7 | 80 | 60 - 100 | 2.7 | 1.1 - 5.6 |
HQ:XSC11 leva C | /Pt | 150 | 30 | 2.7 | 155 | 115 - 200 | 7 | 3 - 16 |
HQ:XSC11 leva D | /Pt | 100 | 50 | 2.7 | 350 | 250 - 465 | 42 | 17 - 90 |